Hey guys, there are a couple of questions I have in regards to your advice. I believe that the 350 is notorious for this problem. Water finds it's way down the inside of the tube, and has nowhere to go. There are no weep holes in the frame. It collects there and begins to rust away. While I believe that you can remedy some situations, it looks like his tube has actually rotted away from the inside, and is very thin. So thin, that I don't think there would be that much meat to hold a weld. While I believe that you could put a patch panel on the outside and weld it on like some have recommended, I don't feel that is an approach I would take. The rust has already formed, and you can't stop rust once it's started. In a matter of time its going to weaken somewhere else. Am I off on my thinking, because I actually want to know. Not trying to be a dick, just want to know if this is something that is done all the time and is safe?